The problems of foundry of Saint-Petersburg and possible ways of their solving are considered.
.
The problems of foundry of Saint-Petersburg and possible ways of their solving are considered.
В промышленных условиях для выплавки стали 45Л опробован модификатор, содержащий щелочноземельные металлы. Установлены зависимости механических свойств и жидкотекучести от количества вводимого модификатора. Определено количество модификатора, позволяющее увеличить вышеуказанные свойства.
The foundry inoculant containing alkali-earth metals for smelting steel brand 45 L was tested in production conditions. Relationship of mechanical properties and castability on the number of the entered inoculant was established. It was defined the number of the inoculant allowing to improve properties.
.
The offered modernization of the mill presumes the increase of capacity of the small-sort wire mill of hot milling 150 approximately till 40% at reduction of cost of the produced on it rolled wire by 15%, that will allow in future as well to grow the volumes of hardware production.
BRITISH STEEL СОБИРАЕТСЯ ОБЪЯВИТЬ О СДЕЛКЕ С КИТАЙСКОЙ ФИРМОЙ JINGYE GROUPАЛЮМИНИЕВЫЙ СПЛАВ ПЕРЕШЕЛ КРИТИЧЕСКУЮ ОТМЕТКУ 500 МПа ПРЕДЕЛА ПРОЧНОСТИ НА РАСТЯЖЕНИЕНОВОЕ ПАРТНЕРСТВО ФИРМЫ »NORICAN GLOBAL A/S»ОПТИМИЗАЦИЯ ТЕХНОЛОГИИ ПРОИЗВОДСТВА ТЯЖЕЛОГО СТАЛЬНОГО ЛИТЬЯТРИ РАЗРАБОТКИ В ОБЛАСТИ ПРОМЫШЛЕННОЙ БЕЗОПАСНОСТИНОВОЕ СВЯЗУЮЩЕЕ, ГАРАНТИРУЮЩЕЕ ЧИСТОЕ СЖИГАНИЕЛИТЕЙНОЕ ПРОИЗВОДСТВО БУДУЩЕГО
.
.
The work of the burden heating outfits for electrosmelting is considered. It is shown that equipping of heating units by the system KIP allows to receive considerable economic and ecological effect.
.
In the article there are examined the problems of using of impulse processing of different intensity for production of cast articles from aluminium alloys.
.
Преждевременное разрушение железобетонных конструкций, подвергаемых агрессивному воздействию окружающей среды, является серьезной проблемой как с технической, так и с экономической точки зрения. Арматура из углеродистой стали, заложенная в бетон, обычно не подвержена коррозии из-за образования защитной ионно-оксидной пленки, которая пассивирует сталь в условиях сильных щелочей в порах бетона. Однако эта пассивность может быть нарушена хлоридами, проникающими через бетон, или из-за карбонизации, достигающей поверхности арматуры. Затем начинается коррозия.Примером решения данной проблемы является замена при строительстве обычной стальной арматуры на плакированную. Через близко расположенные поверхности раздела двух твердых металлов атомы диффундируют между собой с различной скоростью при высокой температуре, определенном давлении. Тем самым, создается металлургическая связь между двумя твердыми металлами, целостность или «прочность» которых зависит от «чистоты» границы раздела между двумя металлами и атомов, составляющих эту «переходную зону» или связь.В статье исследуется плакированный арматурный прокат с целью определения возможности производства в условиях стана 320 ОАО «БМЗ – управляющая компания холдинга «БМК». Для изучения нового вида арматуры были проведены такие виды исследований, как определение химического состава, микроструктуры, механических свойств. Определены основные преимущества данного вида продукции.
Premature destruction of reinforced concrete structures exposed to aggressive environmental influences is a serious problem, both from a technical and economic point of view. Carbon steel reinforcing bar embedded in concrete is usually not subject to corrosion due to the formation of a protective ion-oxide film that passivates the steel under conditions of strong alkalis in the concrete pores. However, this passivity can be disrupted by chlorides penetrating the concrete, or by carbonation reaching the surface of the reinforcing bar. Then the corrosion begins.An example of a solution to this problem is the replacement of conventional steel reinforcement with clad steel during construction. Through the closely spaced interface of two solid metals, the atoms diffuse with each other at different speeds, at a high temperature, and at a certain pressure. This creates a metallurgical bond between two solid metals, the integrity or «strength» of which depends on the «purity» of the interface between the two metals and on the atoms that make up this «transition zone» or bond.The article investigates plated rebar, to determine the possibility of production in a mill 320 OJSC «BSW – Management Company of the Holding «BMC». To study the new type of reinforcing bars, special types of research were conducted as determining the chemical composition, microstructure, and mechanical properties. The main advantages of this type of product are defined in the article.
.
The reasons of low impact strength and high temperature of viscous-fragile transition of the basic metal of gas pipe from steel 17G1С are investigated. It is established that high fragility of metal of pipe is caused by release of the cementite extended inclusions at the border perlite-ferrite by metallographic researches with application of methods of light and dark field.
В работе рассмотрено влияние тиксотропной термической обработки на структурообразование эвтектического алюминиево-кремниевого сплава в зависимости от температуры и времени выдержки вблизи эвтектического равновесия. Проведено теоретическое обоснование процесса на основе данных термоанализа и полученных микроструктур.
The influence of a thixotropic heat treatment on the structure formation of the eutectic aluminum-silicon alloy subject to the temperature and time of exposure near the eutectic equilibriumis giver in the article. The theoretical study of the process based on the data obtained and the thermal analysis of microstructures is made and described.
.
The program ASTRA-4 with thermodynamic database is used in this work fo r thermodynamic modeling of cast alloy, received due to volume alloying by boron. The modeling was carried out by means of several calculations with following specializing of parameters with binary and ternary diagrams of systems.
Обсуждены вопросы возможности повышения эффективности противопригарных покрытий путем использования в их составах наноматериалов. Наноматериалы позволяют интенсифицировать протекание реакций образования эрозионностойкой фазы муллита, которая повышает высокотемпературную когезионную прочность противопригарных покрытий.
Matters on possibility of increase of efficiency the nonstick coverings by means of using nanomaterials in their structures of are discussed. Nanomaterials enable to intensify course of reactions of formation of erosion-resistant phase of mullite which increases high-temperature cohesive solidity of the nonstick coverings.
К 60-летию со дня рождения
Еo the 60* anniversary
.
The backgrounds and history of creation, development of the quality system, and also practice and results of the works on certification of the quality system and production at RUP “BMZ” are considered in the article.
Рассмотрены условия формирования нанокристаллического состояния структуры в углеродистых сталях. Приведены методики проведения исследований и экспериментальные данные о микроструктурном строении упрочненных деталей рабочих органов сельскохозяйственной техники из углеродистых конструкционных сталей пониженной прокаливаемости. Показано, что применение технологии импульсного закалочного охлаждения и низкого отпуска обеспечивают получение стальных изделий с фрагментированной нанокристаллической структурой мартенсита. Фрагментация зерен мартенсита в углеродистых конструкционных сталях при термической обработке деталей существенно повышает их механические характеристики.
The conditions of formation of the nanocrystal state of the structure in carbon steels are considered in the article. The methods of research and experimental data on the microstructural structure of the strengthened parts of the working bodies of agricultural machinery made from carbon steels of the lowered hardenability are given. It is shown that pulsed quenching and low tempering provides of steel products with fragmented nanocrystal structure of the martensite. Fragmentation of martensite grains in carbon structural steels during heat treatment of parts significantly increases their mechanical characteristics.
В НИТУ «МИСиС» с 9 по 12 ноября 2020 г. прошла юбилейная X Международная научно-практическая конференция «Прогрессивные литейные технологии».
.
.
It is shown that using of static thyristor compensation systems improves efficiency, decreases consumption of power and electrodes, but increases the cost of furnaces of alternating current.
.
Analysis of the bowl-crystallizers diameter changing in the process of the belt casting is carried out. The bowlcrystallizers construction providing production of high-accurate casting is worked out.
.
.
.
An attempt of building of physical-mathematical model of thermos-stressed state in the shell of hardening ingot is made.
.
There are given the investigations results of optimization of alloy chemistry for transition zone of bimetallic casts, consisted of steel 45 and steels of 5X3V3MFS, 3X2V8F type. This work is carried out using the simplex-checker method of the mathematical planning of the experiment.
Проведены экспериментальные и исследовательские работы по разработке параметров технологии литья отливок с внутренними полостями, оформляющимися песчаным стержнем, методом литья в облицованный кокиль с вертикальным разъемом. Выявлено влияние литниковых систем с центральным стояком и боковыми стояками на толщину проливаемости стенки отливки и механические характеристики сплава чугуна, в том числе и лигатурами.
The article presents a number of experimental and research works on the development of the parameters of the casting technology for castings with internal cavities formed by a sand rod, by casting in a lined coquille (chill mould) with a vertical connector. The influence of gating systems with a central riser and side risers on the thickness of the casting wall shedding and on the mechanical characteristics of the cast iron alloy, including ligatures, is revealed.
.
By the specific chemical and phase compositions as well as the shape of grains close to spherical the refractory fillers can find application in foundry production as manufactured fillers.
.
The aim of this article is determination of possibility of forming of metal cord lot of construction 2xd without daily equalizing (till the relaxation process ending) subject to changing of residual twisting.
Приведены результаты комплексной оценки условий труда работающих в гальванических цехах, которые получены на основании исследований факторов производственной среды рабочих мест. Приведена гигиеническая классификация рабочих мест гальванических цехов по условиям труда.
The results of complex evaluation of working conditions in galvanic workshops, and based on research of industrial environmental factors jobs are given. The hygienic overview of working conditions classification in working stations of galvanic workshops is given.
.
It is shown that the method of acousto-emission is used for forecasting of the aluminium alloys casting porosity class before pouring by intensity of acoustic emission signals.
.
In the article there is presented the program complex “LENTA ” for modeling of the armored chlorine-copper tape at continuous casting into rolling crystallizer. There are described the possibilities of the software support and form of representation of the calculation results.
.
Peculiarities of technology of the casting «Piston» production for high-loaded diesel engines are considered.
.
UP ‘'Institute BelNIILit" has 40-years operational experience in the foundry market in the field of creation of forming equipment for production of piston rings castings in vertical-stack moulds.
50 лет ОАО «Гомельский литейный завод «ЦЕНТРОЛИТ»
.
Проведен анализ существующих технологий металлургического производства, отличающихся минимальным вредным воздействием на окружающую среду. Выбросы в атмосферу углекислого газа можно исключить при использовании водорода в качестве восстановителя оксидом железа. Лучшие результаты обеспечиваются при получении водорода электролизом воды, но такие технологии требуют серьезных инвестиций. Более реальным в плане создания «зеленых» технологий в металлургическом производстве является снижение потребления природного газа, улавливание отходящих газов металлургического производства и использование их для производства электроэнергии и новых видов продукции: метанола, синтетического спирта, удобрений и полимеров. Составной частью «зеленых» технологий является также реализация концепции NoWASTE, направленной на минимизацию отходов, подлежащих захоронению. Приведены примеры безотходных технологий переработки отходов алюминия на ООО «НПФ «Металлон».
The paper analyzes the existing technologies of metallurgical production with minimal harmful effects on the environment. Emissions of carbon dioxide into the atmosphere can be eliminated using hydrogen as a reducing agent with iron oxide. The best results are realized when hydrogen is produced by electrolysis of water, but such technologies require serious investments. More realistic in terms of creating “green” technologies in metallurgical production is to reduce the consumption of natural gas, capture waste gases of metallurgical production and use them to produce electricity and new types of products: methanol, synthetic alcohol, fertilizers and polymers. An integral part of “green” technologies is also the implementation of the NoWASTE concept, aimed at minimizing waste to be disposed of. Examples of non‑waste technologies for the processing of aluminum waste at OOO NPF Metallon are given.
.
There are not enough of production facilities on crushing of newly-formed slag due to increase of production volume on steel smelting. The tendencies of slag-processing at OAO «BMZ» are considered.
.
It is shown that by means of electroslag casting the ingots of knife billets with necessary configuration with minimal allowances for consequential mechanical processing can be produced.
Предложен метод определения пластичности металлических материалов, реализуемый с помощью динамического индентирования материала сферическим наконечником. Измеряемая величина пластичности определяется соотношением пластической и полной деформаций в образующейся при вдавливании лунке и учитывает влияние модуля упругости материала. Получена зависимость, связывающая пластичность и динамическую твердость материалов. Проведены эксперименты на металлах, имеющих модуль упругости от 70 до 380 ГПа и твердость до 62 HRC.
The method of plasticity test of metallic materials realized by means of a dynamic dimpling of material by a spherical tip is offered. The measured value of plasticity is defined by a ratio of plastic and complete deformations in the formed indentation which considers influence of an elastic modulus of material. The dependence connecting plasticity and dynamic hardness of materials is received. Experiments on metals from 70 to 380 GPA having an elastic modulus and hardness up to 62 HRC are made.
Для обеспечения безопасности эксплуатации зданий и сооружений из железобетона в соответствии с европейскими нормами устанавливаются требования к ее усталостной выносливости (прочности). Испытания проводятся с размахом колебаний 2sa от 150–200 МПа. Арматура должна выдерживать от 1 до 2 млн циклов.Проведен анализ причин снижения усталостной выносливости холоднодеформированной стали. На усталостную выносливость большое влияние оказывает наличие поверхностных дефектов и концентраторов напряжений. В качестве концентратора напряжений в арматуре выступает галтельный переход в месте пересечения поперечного ребра с телом арматуры. Для детального выявления причин преждевременного разрушения был проведен анализ состояния излома в районе утолщенных (маркировочных) ребер. Была установлена последовательность разрушения арматуры и определено место зарождения трещины. Данный излом характеризуется как усталостный с четко выраженными зонами усталостного разрушения с мелкозернистой поверхностью и зоной статического излома – остальной части сечения с волокнистым строением. При нанесении прокатной маркировки нарушались плавность галтельного перехода в месте пересечения поперечного ребра с телом арматуры, что и явилось причиной снижения усталостной выносливости холоднодеформированной арматуры.Приведены результаты разработки требований к прокатному инструменту, который используется при производстве холоднодеформированной арматуры.Использование информации, приведенной в настоящей статье при проектировании, закупке и изготовлении инструмента, позволит минимизировать факторы, отрицательно влияющие на усталостную прочность арматуры.
To ensure safe operation of buildings and structures from reinforced concrete, European norms set requirements for its fatigue strength (resistance). Tests are carried out with oscillation swing amplitude 2sa from 150–200 MPa. Rebar shall withstand from 1 to 2 mln. cycles.The analysis of causes which decrease the fatigue strength of cold-formed steel is made in the article. Fatigue strength is a lot affected by surface defects and stress concentrators. Filler transition in the point where transversal rib crosses a rebar body becomes as a rebar stress concentrator. To detect details of early breakage, analysis the condition of fracture in the area of thickened (marking) ribs was made. Sequence of rebar breakage was established as well as the initial point of a crack creation was detected. This fracture is characterized as a fatigue one, with clear zones of fatigue fracture having fine-grained surface and static fracture zone– the rest of section with fibrous structure. While applying a bar mark, smoothness of filler transition was disturbed in the crossing point where transversal rib crosses a rebar body, and this action caused decrease of fatigue strength of cold-formed rebar.The article describes research on development of requirements for rolling tools used in production of cold-formed rebars.Use of information given in this article during design, purchasing and manufacture of the equipment will allow to minimize factors which have negative influence on rebar’s fatigue test results.
.
There is studied the origin of increase of tendency to cracking of reinforcement bars at production at mill 320 of the Belarussian metallurgical works. On the ground of the carried out integrated study the technology of thermostrengthening of reinforcing steel, providing the required structural status of finished steel production, is developed and introduced.
В работе приведены результаты исследования закономерностей формирования гранулометрического состава, структуры и свойств модифицирующих лигатур с высоким содержанием легирующего компонента для производства хромовых бронз. Изучена кинетика изменений физико‑механических свойств гранулированных композиций в зависимости от температуры в помольной камере и отношения объема рабочих тел к объему шихты. Представлены результаты топографии гранул и их структуры, показывающие, что полученные по оптимальному режиму механического сплавления гранулы представляют собою плотные тела с микровключениями хрома, максимальный размер которых не превышает 15‑20 мкм.По результатам проведенного термодинамического моделирования установлены термодинамически обоснованные тугоплавкие соединения, синтезированные в процессе получения лигатуры, которые должны эффективно выполнять роль модификаторов первого рода, обеспечивая производство бронз с суб‑/микрокристаллическим типом структуры основы.Осуществлена оптимизация процессов компактирования механически сплавленных композиций и исследовано влияние основных технологических факторов – температуры нагрева холоднопрессованных брикетов и коэффициента вытяжки при горячем прессовании на физико‑механические свойства компактных материалов. Представлены результаты изучения структуры и свойств наиболее перспективной композиции Cu – 20%Cr, позволяющие выявить ее микрокристаллический тип, сохраняющийся после длительного высокотемпературного воздействия при переработке гранулированной композиции в полуфабрикат, и сделать вывод о дисперсном характере ее упрочнения, что дополнительно подтверждает данные термодинамического моделирования о возможности механического синтезирования нанокристаллов тугоплавких соединений для выполнения роли модификаторов.По результатам исследований выполнен сравнительный анализ свойств разработанной лигатуры и бериллиевой бронзы, устанавливающие возможность ее применения в качестве самостоятельного материала электротехнического назначения.
The paper presents the results of a study of the regularities of the formation of granulometric composition, structure and properties of modifying ligatures with a high content of alloying component for the production of chrome bronzes. The kinetics of changes in the physico‑mechanical properties of granular compositions depending on the temperature in the grinding chamber and the ratio of the volume of working bodies to the volume of the charge has been studied. The results of the topography of granules and their structure are presented, showing that the granules obtained according to the optimal mode of mechanical fusion are dense bodies with microinclusions of chromium, the maximum size of which does not exceed 15–20 microns.Based on the results of thermodynamic modeling, thermodynamically justified refractory compounds synthesized in the process of obtaining a ligature have been established, which should effectively perform the role of modifiers of the first kind, ensuring the production of bronzes with a sub‑/microcrystalline type of base structure.The processes of compacting mechanically fused compositions were optimized and the influence of the main technological factors – the heating temperature of cold‑pressed briquettes and the extraction coefficient during hot pressing on the physical and mechanical properties of compact materials was investigated. The results of studying the structure and properties of the most promising Cu – 20 %Cr composition are presented, which make it possible to identify its microcrystalline type, which persists after prolonged high‑temperature exposure during the processing of the granular composition into a semi‑finished product, and to conclude about the dispersed nature of its hardening, which additionally confi ms the data of thermodynamic modeling on the possibility of mechanical synthesis of nanocrystals of refractory compounds to perform the role of modifiers.According to the results of the research, a comparative analysis of the properties of the developed ligature and beryllium bronze was performed, establishing the possibility of its use as an independent material for electrical purposes.
.
Methods of selection and appraisal of own technology (product, service, idea) which reflects its readiness for commercialization are offered.
.
.
.
Mechanisms of modification of cast iron and steel\^ were analyzed and thermodinamic performance criterion of modifiers was defined. It is shown that in cast irons, Mg, Ca and P3M mostly act like refining modifiers. In steel they act as refining and surfactant species. Effectiveness of modifiers for steel is determined by their high degassing and surface activity, low distribution coefficient, weak interaction with Ъ-Ре, low activity in liquid metal.
.
The comparative researches of microstructure of highstrength cast iron after laser and plasma processing are carried out. It is shown that the peculiarity of plasma processing is formation of deeper layers with hardness 950010000 MPa. At laser processing the depth of the strengthened layers is less (about 0,5-0,8 mm), and their hardness is higher (to 11000 MPa).
.
It is shown that mechanical and metallographic characteristics of rod, rolled at speed 100 and 105 m/sec, correspond to ZTU 840-03-2006.
Представлены результаты исследования, компьютерного моделирования влияния формы зерна песка на формирование прочности стержневой смеси. Установлена существенная зависимость прочности литейного стержня от качественных характеристик огнеупорного наполнителя.
The results of research, computer simulation of the influence of the shape of the grain of sand on the formation of the strength of the core mixture are presented. An essential dependence of the strength of the core on the quality characteristics of the refractory filler is established.
.
The description of equipment for hydrodynamic experiments and methods of hydromodeling of foundry processes, allowing to carry out three-dimensional modeling of filling process, is given. This method can be used for identification of numerical models and development of casting technology of the new types of production.
Выполнена оценка воздействия порошковых частиц SiC в режиме сверхглубокого проникания (СГП) и последующей термической обработки на изменение параметров тонкой структуры алюминиевого литейного сплава АК12. Импульсное воздействие на сплав обеспечило структурную перестройку материала на разных структурных уровнях. На этой основе из АК12 получен массивный композиционный материал, армированный волоконными зонами с перестроенной структурой.
The estimation of the impact of the SiC powder in the mode of super-deep penetration (SDP) and subsequent heat treatment on the evolution of the fine structure parameters of aluminum casting alloy Al-12%Si are made. Impulse impact on the alloy provided evolution of its structure at different scales. Thus a massive composite material reinforced with the fiber zones was obtained from aluminum alloy casting.
.
The technological process of manufacture of castings out of high-strength case iron in conditions of cast-steel works of Minsk Tractor Plant is described.
.
The advantages and restrictions of the optical copying of inner surfaces with lightguide way systems are analyses.
В статье излагается история становления и развития производства металлокорда в Беларуси. Рассмотрены основные пути, по которым прошел Белорусский металлургический завод от выпуска первой тонны металлокорда до выхода на производственные мощности, в 2 раза превышающие проектные. Много внимания уделено структуре метизного производства, в рамках которого изготавливается визитная карточка завода, людям, которые непосредственно участвовали и участвуют в процессе. Приведена география поставок металлокорда и основным клиентам-потребителям, которые используют данную продукцию при производстве шин. На основании изменения требований автомобильной промышленности прослеживается взаимосвязь изменения свойств металлокорда с момента создания до настоящего времени.
The article describes the history of the formation and development of metal cord production in Belarus. The main ways of the Belarusian metallurgical works had followed from the production of the first tons of steel wire cord, before reaching the production capacity, twofold of the design capacity. The authors paid a lot of attention to the structure of hardware production, which is the visiting card of the plant today, to people who directly participated and promote the process of new products manufacture. Particular attention in the article is devoted to the geography of deliveries of metal cord and the main customers – consumers who use this product in the production of tires. The changes in the properties of the steel wire cord from the moment of first manufacture to the present time is traced, based on permanent changes of the requirements of the automotive industry.
Проведен сравнительный анализ коррозионных свойств цинксодержащих покрытий, полученных на основе металлического порошкового цинка и дисперсного отхода горячего цинкования. Результаты исследования коррозионной стойкости цинксодержащих покрытий электрохимическим методом и в камере солевого тумана показали, что покрытия, полученные на базе дисперсного отхода горячего цинкования, не уступают по защитным свойствам покрытиям на базе порошкового стандартного цинка.
A comparative analysis of the corrosion properties of zinc-containing coatings obtained on the basis of metallic powder zinc and dispersed hot-dip galvanized waste has been carried out. The results of a study of the corrosion resistance of zinc-containing coatings by the electrochemical method and in a salt spray chamber have shown that coatings obtained on the basis of dispersed hot-dip galvanized waste are not inferior in protective properties to coatings based on powder standard zinc.
.
Thе given investigations established positive influence of flux composition, mixing and preparation during processing of dispersion and oxidized wastes of aluminum alloys in short-flame rotary furnace. Substitution of cryolite in chlorine-containing flux with fluorspar is proved advisable.
.
The analysis of technologies of modifying has shown that maximal efficiency is reached at input of additives by the methods allowing to distribute them in regular intervals to distribute them evenly on volume of metal and to provide the minimum charcoal fumes in atmosphere.
.
It is shown that using of modern WEB-technologies will help not only to provide considerably the work on creation of ASUTP applications, but to introduce in it a number of new possibilities as well.
.
.
.
.
.
This work is dedicated to investigation of peculiarity of cinder formation on rolled wire in the process of its cooling immediately after rolling, of the factors influencing on strippability of cinder at testing of the rolled wire samples after rolling and also after 20 and 50 days of storing outdoors.
.
The article provides а mathematical model of steel smelting in a steel-melting arc furnace with provision for calculation of necessary quantity of oxygen for maintenance of preset temperature of steel when arcs are switched off It shows that oxygen supply during the arcs disconnection period secures energy consumption reduction.
.
The improved technology of production of reinforcement no 20 using the developed table of calibration enabled to increase the stability of rolling process due to elimination of technological metal canting in intermediate train and to improve efficiency of mill 320.
Рассмотрено влияние шума на работающих в литейных цехах (распределение профессионального заболевания кохлеарным невритом слухового органа по профессиям и показатели заболеваемости работающих).
Influence of noise on working in foundry shops is considered (distribution of occupational disease cochlear neuritis of an auditory organ by professions and indicators of incidence of working).
.
.
Определены молярная объемная энергия Гиббса и молярная граничная энергия железа в зависимости от температуры. Показано, что фазовые превращения в железе происходят в термодинамически равновесных условиях. Микрокристаллы фаз железа являются дендритами. Кристаллизация расплава железа – наноструктурный процесс. Показано, что перекристаллизация железа является в основном диффузным процессом.
Gibbs molar volumetric energy and iron boundary molar energy are determined depending on temperature. It has been shown that phase transformations in iron occur under thermodynamically equilibrium conditions. The iron phase microcrystals are dendrites. Crystallization of the iron melt is a nanostructural process. Iron recrystallization has been shown to be a largely diffuse process.
.
It is shown that introduction of statistical method of control will allow to reduce efforts for production, delivery of the samples to the laboratory of mechanical testing, and to reduce the expenses as well.
,
The development of the technology of the cutting teeth plastic forming on the surface of segment instead of milling is presented.
.
\
.
The method of computer modeling, synthesizing cell- automatic approach and equations of termoelasticity for the processes, proceeding at crystallization of metal invironment, is offered. The three-dimensional computer calculations of the structure such as ’’cross", filled by aluminium alloy, having a nonuniform temperature field, received during filing of the mold by metal, are carried out.
Максимальная вытяжка катанки при однократном волочении характеризует ее деформационную способность до сверхбольших суммарных обжатий. Предложен определяемый при растяжении комплексный показатель деформируемости низкоуглеродистой катанки, учитывающий способность металла к упрочнению и его склонность к локализации пластической деформации.
The maximum drawing of the wire rod with a single drawing characterizes its deformation ability to extremely large total compressions. A complex index of deformability of a low-carbon wire rod determined under tension is proposed, taking into account the ability of the metal to harden and its tendency to localize plastic deformation.
.
The groups of alloy steel scrap. suitable for wear-resistant synthetic chromium and iron grades ich18VN ich18VM are studied and defined. Found that the number of alloyed steel scrap in the charge for these irons can be more than 85%, and the price of the charge decreases from 30 to 45%.
.
The data on investigation of optimization of technical-economical indices of the chamber furnace operation (heating furnace PVP-1) are given.
.
One of the color programs for modeling of volume stamping by means of QF0RM3D is considered.
.
The temperature-deformation criterion of assessment and optimization of routes of the thin high-carbon wire drawing enabling to increase plastic properties of wire at retaining of its durability is offered.
.
The laboratory-scale plants for production o f standard measuring samples of sand and core blends developed by N P RUP ''Institute BelNIIlit'’ for the processes of cores and molds production in heated and non-heated accessories are presented.
.
The problem of the mathematic modeling of the mass transfer processes in liquid metal in conditions of its degassing by complex vacuum influence on melt, of blowout with inert gas and of electrostatic field is discussed. New data — phenomenon of “electrodynamic induction” is attracted for arrangement of boundary condition on the surface vacuum-moving metal”
.
Increase by 30–40% the linear speed of solidification of ingot with diameter 100 mm, to produce the castings with eutectic modified microstructure.
.
The numerical analysis of dynamics of the cindery particle moving in the system ''riser-gate channel'' is presented. The dependencies of the cindery particle speed on the period of its moving, denseness, radius and proportion of sectional area of riser and feeder are calculated.
.
The process of computer development of casting geometrical model and engineering of mold elements is examined.
.
The main stages of the program of assimilation of new types of production for big- and superbig-volume tires at RUP '‘BMZ” are given.
В работе представлены результаты экспериментальных исследований по нанесению покрытий порошком EuTroLoy 16006.04 с помощью плазменно-порошковой наплавки. Анализ макроструктуры позволил установить частичное отсутствие пор, несплавлений и трещин между подложкой и наплавленным слоем. Установлены различия в фазовом составе и в механических свойствах покрытий. В местах нанесения плазменно-порошковой наплавки выявлено повышение твердости.
The paper presents the results of experimental studies on the surface coating of powder EuTroLoy 16006.04 with the help of plasma-powder overlaying. Analysis of the macro-structure made it possible to establish a partial absence of pores, fusions and cracks between the sub-spoon and the deposited layer. Differences in the phase composition and in the mechanical properties of the coatings were established. In places of application of plasma-powder overlaying an increase in hardness has been revealed.
Рассматриваются способы и структуры информационно-технологической оценки состояния поверхностей в труднодоступных областях отливок и проката.
Ways and structures of information and technological assessment of surfaces sate in nooks of castings and rolling are considered.
В статье сравниваются различные аспекты производства тормозных дисков с использованием вертикальных безопочных формовочных линий и горизонтальных формовочных линий с горизонтальной полостью разъема. Показаны преимущества инвестиционных затрат вертикальной формовки и годового потребления энергии формовочных линий технологии DISAMATIC по отношению к отливкам. Приводится сравнение двух формовочных технологий на основе производственных данных литейного завода Сунгво (Южная Корея), производящего тормозные диски для Hyundai. Демонстрируются преимущества формовочной технологии DISAMATIC в плане затрат на инструменты и энергозатрат
The article compares different aspects of brake disc production using vertically parted flaskless molding lines and horizontal parted tight flask molding lines. In the first section the vertical molding process demonstrates advantages in terms of investment costs. Furthermore, annual energy consumption of the molding lines in relation to castings produced is discussed, again demonstrating clear benefits from the Disamatic-technology. In the second section a comparison between two molding technologies for the production of brake discs is made on the basis of production data from the South Korean foundry Hyundai Sungwoo. The Disamatic molding process, however, offers advantages in terms of tooling costs and energy consumption.
.
The numerical analysis of temperature field, being cooled under analytical and numerical schematic models, is carried out. It is shown that implicit schematic model is close to analytical decision.
Дано описание разработки системы, позволяющей проследить все этапы контроля качества проволоки для рукавов высокого давления, начиная с механических испытаний и заканчивая отгрузкой потребителю.
The description of development of the system, enabling to trace all the stages of qualit y control of wire of the high pressure cantilevers, starting from mechanical tests and finishing with delivery to consumer, is given.
.
The methods of appraisal of technical state of rotor equipment by vibration, applied at RUP «BMZ» for diagnostics of the basic and auxiliary equipment of the mills are examined.
.
The carried out team-work of NIIZHB and RUP “BMZ” enabled to receive new technological decisions at production of bale reinforcing bar, realization of which will increase reliability of reinforced-concrete constructions of buildings and installations.
.
The article gives solution to the 3-D problem of hydrodynamics and heat transfer in the process offiling the intermediate ladle of the continuous billet casting machine.
Представлены результаты исследования фазово-структурных превращений, протекающих при механическом легировании композиций систем «основной металл – легирующий оксид – легирующий металл с высоким сродством к кислороду», направленного на установление места и роли в этом процессе термодинамического фактора.
The paper presents the results of the research in phase-structured transformation proceeding in the process of mechanical alloying of compositions of systems «parent metal – alloying oxide – alloying metal with high oxygen affinity, aimed at determining the place and function of the thermodynamic agent in this process.
.
It is shown that the mains soil pollutants, adjacent to RUP are copper, zinc, nickel, lead. The main reason of soil solution is its production activity.
Изучено извлечение катионов Fe3+ и Pb2+ из водных растворов материалом, полученным на основе сталеплавильного шлака. Установлено, что процесс очистки воды от ионов Fe3+ и Pb2+ данным материалом происходит по смешанному механизму как за счет образования труднорастворимых силикатов, так и за счет образования гидроксидов. При изменении скорости фильтрации от 2 до 10 колоночных объемов в час процент сорбции остается в пределах 91,5–99,8. По эффективности извлечения наиболее оптимальной является скорость фильтрации, равная 6 колоночным объемам в час. Материал на основе сталеплавильного шлака способен поглощать ионы Fe (III) до 5 мг-экв/г и при совместном осаждении 0,64–1,27 мг-экв/г ионов Pb (II).
The aim of the present paper is investigation of removal of Fe3+ and Pb2+ ions from aqueous media by material on the basis of steel melting slag. It has been established that the process of water purification from Fe3+ and Pb2+ ions by this material proceeds by a mixed mechanism both due to the formation of slightly soluble silicates and also due to the formation of hydroxides. When the filtration rate varies from 2 to 10 column volumes per hour, the percentage of sorption remains within 91,5–99,8%. The most optimal filtration rate is 6 column volumes per hour. Material on the basis of steel melting slag absorbs of Fe (III) up to 5 mg-eq/g and Pb (II) 0.64–1.27 mg-eq/g.
.
.
.
The main directions and developments of Program “Metallurgy” for years 2007–2010 are given.
.
The field of application of castings of pure copper is shown. The main factors influencing on the copper casting quality are determined and analyzed. It is determined that the main element of the technological process of the production of alloys of copper, influencing on the casting quality, is proportion of mixture and its preparation before melting
60 лет со дня рождения
.
.
There is shown, how modification of the rare-earth metals influences on crack-resistance of the cast boron-containing material.
Показано, что кристаллизация чугунов является наноструктурным процессом. Аустенитно-графитная эвтектика формируется из нанокристаллов железа и графита, свободных атомов железа и графита. Аустенитно-цементитная эвтектика образуется из нанокристаллов железа и графита, свободных атомов графита и железо-углеродных комплексов. Первичные микрокристаллы аустенита формируются из нанокристаллов железа, графита и железоуглеродных комплексов.
Crystallization of cast iron has been shown to be a nanostructured process. Austenitic-graphite eutectic is formed from iron and graphite nanocrystals, free iron and graphite atoms. Austenitic-cementite eutectic is formed from iron and graphite nanocrystals, free graphite atoms and iron-carbon complexes. Primary austenite microcrystals are formed from iron nanocrystals, graphite and iron-carbon complexes.
.
The computer simulation of the characteristics of manufacturing technology of the iron casting «body» for different correlations of feeder, slag traps and riser, recommended for the molds obtained by vacuum-film forming is carried out. The volume evolution of filling of the casting is calculated and dependences of speed instability and its projections on period of filling in assigned points of the mold are established.
Проанализированы основные подходы в модифицировании силуминов. Приведены результаты воздействия различных комплексных модификаторов на структуру и свойства алюминиево-кремниевых сплавов. Рассмотрены перспективы создания силуминов, отличающихся не только прочностными, но и пластическими свойствами.
The principal approaches to modification of silumins have been analyzed. Results of the effect of various complex modifying agents on the structure and properties of aluminum-silicon alloys have been presented. Prospects of production of silumins that are different not only in strength properties but also in plastic properties have been analyzed.
.
The given investigations proved the increase of heat resistance of piston alloy AK12M2MgN at increasing in its contents of iron till 1% at additional processing of alloy by fluozirconate potassium and sulfur.
.
The article shows the controllability of initial solidification temperature of AК7 (ALSi7Mg) alloy by the chemical compounds inserted into liquid alloy in mixture form giving exothermic effect. There are presented the results in graphical form of influence of mixture compounds on the studied temperature on w/w