limЛитье и металлургияLitiyo i Metallurgiya (FOUNDRY PRODUCTION AND METALLURGY)1683-60652414-0406BNTU10.21122/1683-6065-2020-3-36-40lim-3231Research ArticleЛитейное производствоFoundryВлияние легирующих элементов и термической обработки на механические свойства хромистого чугунаInfluence of alloying elements and heat treatment on the mechanical properties of chromium cast ironМаруковичЕ. И.MarukovichE. I.

г. Могилев, ул. Бялыницкого-Бирули, 11

info@itm.byИльюшенкоВ. М.IlyushenkoV. M.

г. Могилев, ул. Бялыницкого-Бирули, 11

ПумпурВ. М.PumpurV. A.

г. Могилев, ул. Бялыницкого-Бирули, 11

АндриенкоВ. М.AndrienkoV. M.

г. Могилев, ул. Бялыницкого-Бирули, 11

ДуваловП. Ю.DuvalovP. Yu

г. Могилев, ул. Бялыницкого-Бирули, 11

Институт технологии металлов НАН БеларусиБеларусьInstitute Technology of Metal of National Academy of Sciences of BelarusBelarus202020102020033640Copyright © Марукович Е.И., Ильюшенко В.М., Пумпур В.М., Андриенко В.М., Дувалов П.Ю., 20202020Марукович Е.И., Ильюшенко В.М., Пумпур В.М., Андриенко В.М., Дувалов П.Ю.Marukovich E.I., Ilyushenko V.M., Pumpur V.A., Andrienko V.M., Duvalov P.Y.Данная работа распространяется под лицензией Creative Commons Attribution 4.0.This work is licensed under a Creative Commons Attribution 4.0 License.https://lim.bntu.by/jour/article/view/3231

Описаны результаты экспериментальных исследований по определению влияния легирования и термической обработки на механические свойства высокохромистого чугуна. При легировании расплава никелем, молибденом и марганцем, а также при термической обработке закалкой изучены удельный износ, предел прочности при изгибе полученных образцов, их твердость и микротвердость. Выполнен сравнительный анализ влияния легирующих элементов и способов термической обработки. При легировании Ni, Mo и Mn наибольший удельный износ имеют литые образцы, не подвергавшиеся термической обработке. Установлено, что наибольшую прочность при изгибе имеют закаленные образцы, легированные Ni, значительно меньшую твердость и микротвердость – литые образцы, не подвергавшиеся термической обработке. Определен примерный состав хромистого чугуна для дальнейших исследований по увеличению его износостойкости. Результаты исследований используются в процессе изготовления деталей дробильно-размольного оборудования.

The results of experimental studies to determine the effect of alloying and heat treatment on the mechanical properties of the high-chromium cast iron are described. When alloying the melt with nickel, molybdenum and manganese, as well as during heat treatment by quenching, specific wear, tensile strength in bending of the obtained samples, their hardness and microhardness were studied. A comparative analysis of the influence of alloying elements and heat treatment methods has been performed. When alloying Ni, Mo, and Mn, cast specimens that have not undergone heat treatment have the highest specific wear. It was established that the hardened Ni alloyed samples have the greatest bending strength. It was found that cast samples that were not subjected to heat treatment have much lower hardness and microhardness. The approximate composition of chromium cast iron was determined for further studies to increase its wear resistance. The research results are used in the manufacturing process of parts for crushing and grinding equipment.

износостойкий хромистый чугунлегирование хромистых чугуновтермическая обработкамеханические свойстваwear-resistant chrome cast ironalloying of chrome cast ironheat treatmentmechanical propertiesReferencesMaja M. E., Maruma M. G., Mampuru L.A., Moema S. J.. Effect of niobium on the solidification structure and properties of hypoeutectic high‑chromium white cast irons // Journal of the Southern African Institute of Mining and Metallurgy. 2016. Vol. 38. No. 10, P. 981–986.Maja M. E., Maruma M. G., Mampuru L.A., Moema S. J. Effect of niobium on the solidification structure and properties of hypoeutectic high‑chromium white cast irons. Journal of the Southern African Institute of Mining and Metallurgy, 2016, Vol. 38, no. 10, pp. 981–986.Atabaki Mehdi Mazar, Jafari Sajjad, Abdollah-pour Hassan Abrasive Wear Behavior of High Chromium Cast Iron and Hadfield Steel – A Comparison // Journal of Iron and Steel Research, International. 2012. Vol. 19(4). P. 43–50.Atabaki Mehdi Mazar, Jafari Sajjad, Abdollah-pour Hassan. Abrasive Wear Behavior of High Chromium Cast Iron and Hadfield Steel – A Comparison. Journal of Iron and Steel Research, International, 2012, vol. 19(4), pp. 43–50.Chung R. J., Tang X., Li D. Y., Hinckley B., Dolman K. Microstructure refinement of hypereutectic high Cr cast irons using hard carbide‑forming elements for improved wear resistance // Journal Wear. 2013. No. 301. P. 695–706.Chung R. J., Tang X., Li D. Y., Hinckley B., Dolman K. Microstructure refinement of hypereutectic high Cr cast irons using hard carbide‑forming elements for improved wear resistance. Journal Wear. 2013, no. 301, pp. 695–706.Марукович, Е. И. Изучение износостойкости деталей из хромистых чугунов, полученных литьем в кокиль / Е. И. Марукович, В. М. Ильюшенко, П. Ю. Дувалов, А. И. Калентионок, К. Э. Барановский // Современные методы и технологии создания и обработки материалов: X Междунар. науч.‑техн. конф. Минск: ФТИ НАН Беларуси, 16–18 сент. 2015. С. 52–57.Маrukovich Е. I., Ilyushenko V. М., Duvalov P. J., Kalentionok А. I., Baranovski K. E. Izuchenie iznosostoykosti detaley из khromistykh chugunov, poluchennykh lityom v kokil [Study of the wear resistance of parts made of chrome cast iron obtained by casting in a chill mold]. Sovremennye metody i tekhnologii sozdaniya i obrabotki materialov = Modern methods and technologies for the creation and processing of materials, Мinsk, FTI of NAS of Belarus Publ., 2015, pp. 52–57.