STABILITY OF THE FAST-QUENCHED ALUMINUM ALLOYS MICROSTRUCTURE
Abstract
The conducted researches of continuous stability of microstructures of the fast-quenched tapes from alloys of aluminum and chrome showed that the natural aging accompanied by discharge of stable phases is observed in copper-bearing alloys. There are no changes in microstructure in the chrome-bearing fast-chilled tapes that confirms their high temporary stability.
About the Authors
A. S. Kalinichenko
Belarusian National Technical University
Belarus
Belarus
V. A. Kalinichenko
Belarusian National Technical University
Belarus
Belarus
V. S. Niss
Belarusian National Technical University
Belarus
Belarus
S. V. Grigoryev
Belarusian National Technical University
Belarus
Belarus
References
1. Калиниченко А. С., Бергманн Г. В. Управляемое направленное затвердевание и лазерная обработка: теория и практика. Мн.: Технопринт, 2001.
2. Марукович Е. И., Стеценко В. Ю., Баранов К. Н. Исследование литья полых заготовок из силумина АК18 методом намораживания на водоохлаждаемом стержне // Литье и металлургия. 2011. № 3. С. 65–67.
3. Ovchinnikov V. I., Roman O. V., Usherenko S. M., Kalinichenko A. S. Effect of Processing with Highspeed Particles and Explosion Energy on Mechanical Properties of Materials // Shock-Assisted Synthesis and Modification of Materials. Eds. AA. Deribas, Yu. B. Scheck.Moscow: Torus Press Ltd. 2006. P. 96–97.
4. Кезик В. Я., Калиниченко А. С. Упрочнение литых макрогетерогенных композитов // Литье и металлургия. 2004. № 1. С. 40–44.
5. Калиниченко А. С. Применение неравновесных процессов затвердевания для получения материалов с улучшенными свойствами // Литье и металлургия. 2010. № 4. С. 49–54.
Review
For citations:
Kalinichenko A.S., Kalinichenko V.A., Niss V.S., Grigoryev S.V. STABILITY OF THE FAST-QUENCHED ALUMINUM ALLOYS MICROSTRUCTURE. Litiyo i Metallurgiya (FOUNDRY PRODUCTION AND METALLURGY). 2014;(1):93-96. (In Russ.)
Views:
441
Email this article 