RESEARCH OF COMPONENTS OF DIRECT THERMAL METHOD OF THE UNDENDRITIC MORPHOLOGY RECEIPT
Abstract
Components of direct thermal method were studied separately. It was found that main cause for non dendrite pattern formation is presence of melt fl w. The role of thermal balance reduced to provision of conditions to motion of the melt under liquidus temperature. Incoming flow resulted in splitting of crystal interface.
About the Authors
E. I. Marukovich
Institute of Technology of Metals of NAS of Belarus
Belarus
Belarus
A. G. Borisov
Physico-technological institute of metals and alloys of the NAS of Ukraine
Ukraine
Ukraine
A. I. Semenechenko
Physico-technological institute of metals and alloys of the NAS of Ukraine
Ukraine
Ukraine
Ju. A. Lebedinskiy
Institute of Technology of Metals of NAS of Belarus
Belarus
Belarus
A. M. Branovitskyj
Institute of Technology of Metals of NAS of Belarus
Belarus
Belarus
References
1. Sim J. G., Choi B. H., Yang Y. S., Kim J. M., Hong C. P. Development of a nucleation accelerated semisolid slurry making method and its application to rheo-diecating of ADC10 alloy // ISIJ International. 2010. Vol. 50. N 8. P. 1165–1174.
2. Brown D. J., Hussey M. J., Carr A. J., Brabazon D. Direct thermal method: new process for development of globular alloy microstructure // International journal of cast metals research. 2003. Vol. 16. N 4. Р. 418–426.
3. Борисов А. Г. Методы реолитья, перспективные для малого производства изделий из алюминиевых сплавов // Процессы литья. 2013. № 4. C. 33–46.
4. Carr A. J., Brown D. J., Hussey M. J., Lumsden N., S c a l a n M. Modelling and experimental development of the direct thermal method of rheocasting // International journal of cast metals research. 2007. Vol. 20. N 6. Р. 325–332.
5. Борисов А. Г. Розеткова та дендритна морфологія первинної фази при литті алюмінієвого сплаву в металевий кокіль // Металознавство та обробка металів. 2010. № 4. С. 13–18.
6. Марукович Е. И., Брановицкий А. М., Лебединский Ю. А. Моделирование роста дендритов при кристаллизации с малым переохлаждением силуминовых сплавов на основе метода фазового поля // Весці НАН Беларусі. Сер. фіз.-тэхн. навук. 2009. № 1. С. 4–13.
Review
For citations:
Marukovich E.I., Borisov A.G., Semenechenko A.I., Lebedinskiy J.A., Branovitskyj A.M. RESEARCH OF COMPONENTS OF DIRECT THERMAL METHOD OF THE UNDENDRITIC MORPHOLOGY RECEIPT. Litiyo i Metallurgiya (FOUNDRY PRODUCTION AND METALLURGY). 2013;(4):24-28. (In Russ.)
Views:
1948
Email this article 