STRUCTURAL AND TECHNOLOGICAL ASPECTS OF DECREASE IN WIRE ANNEALING AT A TWIST OF A HIGH-STRENGTH METAL CORD
Abstract
Deformation by drawing with the raised share of the squeezing tension and application of additional deformation with small degrees in the line of a drawing camp allow to minimize a wire annealing of a cold-deformed wire during a twist of a highstrength metal cord.
References
1. Fetisov V. P., Birjukov B. A. Vlijanie tehnologii svivki metodom dvojnogo kruchenija na formirovanie ostatochnyh kruchenij i prjamolinejnosti metallokorda [Influence of technology lay in a double torsion on the formation of residual torsion and straightness of steel cord]. Lit’e i metallurgija = Foundry production and Metallurgy, 2012, no. 4, pp. 45–47.
2. Fetisov V. P. Priroda izmenenija svojstv holodnodeformirovannoj provoloki v processe svivki vysokoprochnogo metallokorda [The nature of changes in the properties of cold-wire in the process of high-strength steel cord stranding]. Lit’e i metallurgija = Foundry production and Metallurgy, 1997, no. 1, pp. 8–10.
3. Birjukov B. A., Feoktistov Ju. V., Vedeneev A. V. Snizhenie obryvnosti vysokoprochnoj provoloki pri svivke iz nee metalokorda na mashinah dvojnogo kruchenija [Reducing the high wire breakage during coiling of steel cord on her double twisting machines]. Lit’e i metallurgija = Foundry production and Metallurgy, 2012, no. 4, pp. 29–34.
4. Kardonskij V. M., Kurdjumov G. V., Perkas M. D. Tonkaja struktura holodnodeforirovannoj vysokouglerodistoj stali [The fine structure of cold high-carbon steel]. FMM, 1963. T. 15. Vyp. 2, pp. 244–253.
5. Fetisov V. P. Deformacionnoe starenie stali pri volochenii provoloki [Strain aging steel with wire drawing]. Minsk, Belorgstankinpromizdat Publ., 1996, 120 p.
6. Fetisov V. P. Deformacionnoe uprochnenie uglerodistoj stali [Strain hardening of carbon steel]. Moscow, Mir Publ, 2005, 200 p.
7. Fetisov V. P. Plastichnost’ vysokoprochnoj provoloki [The ductility of high strength wire] Moscow, Intermet Inzhiniring Publ., 2011, 128 p.
Review
For citations:
Fetisov V.Р. STRUCTURAL AND TECHNOLOGICAL ASPECTS OF DECREASE IN WIRE ANNEALING AT A TWIST OF A HIGH-STRENGTH METAL CORD. Litiyo i Metallurgiya (FOUNDRY PRODUCTION AND METALLURGY). 2016;(4):62-65. (In Russ.)
Views:
435
Email this article 