APPLICATION OF THERMAL-CYCLIC PROCESSING FOR INCREASE OF STRUCTURE HOMOGENEITY OF BIG CASTINGS OF ALLOY A206
Abstract
The investigation of influence of thermo-cyclic processing (TCP ) in the range of temperature 545-440 °C and ageing at 170 °C, 7 hours on forming of structure and mechanical characteristics of casting alloys A206 with size 100x100x100 mm is carried out. It is determined that at TCP the dispersion of microstructure is increased practically two times as much as compared to standard processing (T6).
About the Authors
E. I. Marukovich
Institute of Technology of Metals of the NAS of Belarus
Belarus
Belarus
A. G. Anisovich
Physical-Engineering Institute of the NAS of Belarus
Belarus
Belarus
G. H. Kimm
Korean Institute of Machines and Materials
Korea, Republic of
Korea, Republic of
K. I. Choj
Belorussian-Korean center of technical cooperation
Korea, Republic of
Korea, Republic of
References
1. Физические основы термоциклической обработки стареющих сплавов / Р.Л. Тофпенец, И.И. Ш иманский, А Т. Анисович, А.Д. Грешилов. Мн.: Наука и техника, 1992.
2. Федюкин В.К. Метод термоциклической обработки металлов. Л.; ЛГУ. 1987.
3. Биропт B.C., Заиграйкина Б.С. Структура и свойства литейных алюминиевых сплавов после термоциклирования // Литейное производство. 1982. № 7. С. 15-16.
4. Кенис М.С., Трахтенберг Б.Ф., Трошина Л.В. и др. Перераспределение легирующих элементов в сплаве Д16 при ТЦО // Термоциклическая обработка металлических изделий. 1982. С. 144-146.
5. Терентьев В.Ф.// Докя. АН СССР. 1969. Т. 185. №2. С. 324-327.
6. Анисович А.Г., Тофпенец Р.Л. Специфика структурообразования в алюминиевых сплавах при термоциклировании // Металлы. 2000. №2. С. 73-78.
Review
For citations:
Marukovich E.I., Anisovich A.G., Kimm G.H., Choj K.I. APPLICATION OF THERMAL-CYCLIC PROCESSING FOR INCREASE OF STRUCTURE HOMOGENEITY OF BIG CASTINGS OF ALLOY A206. Litiyo i Metallurgiya (FOUNDRY PRODUCTION AND METALLURGY). 2006;(3):84-89. (In Russ.)
Views:
414
Email this article 