MATHEMATICAL MODELING OF FORMING OF THE EUTECTIC SILUMIN
Abstract
The numerical model of hardening of continuouslycasted eutectic silumin is worked out. The average speed of enthalpy decreasing in different geometrical zones of casting is calculated on its basis. The experimental samples of the continuously casted eutectic silumin microstructure are received.
About the Authors
E. I. Marukovich
Institute of Technology of Metals of the NAS of Belarus
Belarus
Belarus
A. M. Branovitskij
Institute of Technology of Metals of the NAS of Belarus
Belarus
Belarus
Ju. A. Lebedinskij
Institute of Technology of Metals of the NAS of Belarus
Belarus
Belarus
References
1. Chen W. et al. The Role of Dendrite Arm Spacing in Fatigue of Aluminum Castings // Advances in Aluminum Casting Technology. ASM International. 1998.
2. Thevoz Ph., Desbiolles J.L., Rappaz M. Modeling of Equiaxed Microstructure Formation in Casting / Ph. Thevoz // Metallui:gical Transactions A. 1989. Vol. 20A. P. 311—322.
3. Oldfield W. A Quantitative A pproach to Casting Solidfication. Freezing of Cast Iron // ASM Trans. 1966. Vol. 59. P. 945-960.
4. Брановицкий A.M., Станюленис Ю.Л., Л ебединский Ю.А. Уточнение коэффициентов теплопередачи для решения задачи затвердевания цилиндрических непрерывнолитых заготовок с использованием экспериментальных температурных данных кристаллизатора в установившемся режиме литья // Литье и металлургия. 2005. №1. С 91-93.
5. Marukovich ЕЛ., Branovitsky A.M. Threedimensional thermal model of solidification of continuous casted rectangular billets // The 4-rd International Conference Simulation, Designing and Control of Foundry Processes 25—26 November 1999, Krakow, Poland.
6. Марукович E. И., Брановицкий A.M. Трехмерная тепловая модель процесса непрерывного литья прямоугольных биметаллических заготовок // Докл. НАН Беларуси. 2001. Т. 45. №2.
7. S. - h. Cho, Т. Окапе, Т. Umeda. CA-DFD analysis of nucleation parameter effects on the grain structures of casting // Int. J. Cast Metals Res. 2001. Vol. 13. P. 327-335.
8. Hague M.M., Ismail A F. Effects of cooling rate on structure and properties of Aluminium-Silicon Alloys // Proceedings of 65“ world foundry congress. 2002.
9. Napolitano R.E., Meсо Н., Jung C. Faceted solidification Moфhologies in low-growth-rate A l-S i eutectics // JOM. 2004. Vol. 56. N. 4. P. 16-21.
10. McDonald S., Dahle A., Taylor J., StJohn D. Eutectic Grains in Unmodified and Strontium -Modified Hypoeutectic Aluminum -Silicon Alloys //Metallurgical and materials transactions A. 2004. Vol. 35A.
Review
For citations:
Marukovich E.I., Branovitskij A.M., Lebedinskij J.A. MATHEMATICAL MODELING OF FORMING OF THE EUTECTIC SILUMIN. Litiyo i Metallurgiya (FOUNDRY PRODUCTION AND METALLURGY). 2006;(3):156-160. (In Russ.)
Views:
397
Email this article 