STUDY OF THE EFFECT OF MODIFIERS WITH ULTRADISPERSED PARTICLES IN THE COATING OF THE ELECTRODE FOR MANUAL ARC WELDING ON THE TECHNOLOGICAL PARAMETERS IN MANUFACTURE OF THE ELECTRODE

It is established that inclusion of the modifier into the electrode coating allowed to change the grains of the weld metal from 20–60 to 10–30 mm, to change its morphology and to improve the welding-technological properties of the coated electrode. It is shown that the modifying additive introduced into the coating of a welding electrode containing ultrafine particles in an amount of 1% of the weight of the dry charge had not deteriorated the technological parameters during manufacture, and the integral index of the different thickness (Desp) of electrodes with standard and experimental coatings did not add to the accepted value of 0.05. This indicates that the quality of the lubricating mass, its properties, the stability of the mass flow from the spinneret are satisfactory for both batches.

1. Gordin S. O., Smirnov A. N., Knjaz’kov V. L. Vlijaja ul’tramelkorazmernyh komponentov jelektrodnyh pokrytij na mehanicheskie svojstva metalla shva [Influencing ultra-fine-sized components of electrode coatings on the mechanical properties of weld metal]. Vesnik Kuzbasskogo gosudarstvennogo tehnicheskogo universiteta = Bulletin of the Kuzbass State Technical University, 2012, no. 6(94), pp. 101–104.

2. Urbanovich N. I., Radchenko A. A., Ignatovich Z. V., Baranovskij K. E., Provorova I. B., Rozenberg E. V. Ocenka vlijanija modificirujushhih dobavok v pokrytii elektrodov marki UONI-13/55 na glubinu proplavlenija stali marki St.3 i mikrostrukturu naplavlennogo metalla [Evaluation of the influence of modifying additives in the coating of electrodes of the grade UONI-13/55 on the penetration depth of steel grade St.3 and the microstructure of the weld metal]. Respublikanskiy mezhvedomstvennyy sbornik nauchnyh trudov «Metallurgija» = Republican interdepartmental collection of scientific works «Metallurgy». Minsk, BNTU Publ., 2017, vyp. 38, pp. 138–145.

3. Sokolov G. N., Lysak I. V., Troshkov A. S. i dr. Modificirovanie naplavlennogo metalla nanodispersnymi karbidami vol’frama [Modification of the weld metal by nanodispersed tungsten carbides]. Fizika i himija obrabotki materialov = Physics and chemistry of material processing, 2009, no. 6, pp. 41–47.

4. Parshin S. G. Vlijanie aktivirujushhih fljusov na formirovanie svarnyh shvov pri ruchnoj argonodugovoj svarke [Influence of activating fluxes on the formation of welded joints with manual argon-arc welding]. Svarochnoe proizvodstvo = Welding production, 2000, no. 10, pp. 23–26.

5. Pohodnja I. K., Makarenko V. D., Milichenko S. S. Vlijanie jekscentrichnosti pokrytija na svarochno-tehnologicheskie svojstva elektrodov i kachestvo naplavlennogo metalla [The influence of the eccentricity of the coating on the welding-technological properties of electrodes and the quality of the welded metal]. Avtomaticheskaya svarka = Automatic welding, 1985, no. 11, pp. 39–40.

6. Ovchinnikov V. A., Bazhenov V. V. Vlijanie geometrii jelektrodnyh pokrytij i nalichija defektov v nem na nadezhnost’ zashhity plavjashhegosja metalla ot vozdejstvija vozduha [Influence of the geometry of electrode coatings and the presence of defects in it on the reliability of protecting the melting metal from the effects of air]. Svarochnoe proizvodstvo = Welding production, 1978, no. 5, pp. 39–40.

7. Marchenko A. E. Raznotolshhinnost’ pokrytija kak indikator sostojanija processa i kachestva izgotovlenija svarochnyh jelektrodov [Thickness of the coating as an indicator of the state of the process and the quality of manufacturing of welding electrodes]. Elektrodnoe proizvodstvo na poroge novogo tysjacheletija = Electrode production on the threshold of a new millennium. Cherepovec, associacija «Elektrod» Publ., 2000, pp. 124–125.

8. Vornovickij I. N. Raznotolshhinnost’ pokrytija – osnovnoj pokazatel’ kachestva jelektroda [Thickness of coating – the main indicator of the quality of the electrode]. Svarochnoe proizvodstvo = Welding production, 1989, no. 4, pp. 7–19.

9. Vornovickij I. N. Praktika snizhenija raznotolshhinnosti pokrytija svarochnyh jelektrodov [The practice of reducing the thickness of the coating of welding electrodes]. Svarshhik = Welder, 2000, no. 19(11), pp. 5–9.