Study of the possibility of plasticity increase of cast alloy D16
Abstract
The influence of the high-temperature thermal cycling (HTTC) regimes on structure and high-temperature plasticity of the cast alloy DI6 is investigated. There is shown the principle possibility of single-piece HTTC of cast alloy under conditions of high-speed (electrocontact and induction) heating instead of homogenization. The optimal HTTC conditions are established.
About the Authors
R.L. Topfenets
Belarusian National Technical University
Belarus
Belarus
A. G. Anisovich
Physical-Engineering Institute of the NAS of Belarus
Belarus
Belarus
L. A. Vasiljeva
Belarusian State University
Belarus
Belarus
References
1. Тофпенец Р. Л., Шиманский И.И., Анисович А. Г., Грешилов А. Д. Физические основы термоциклической обработки стареющих сплавов. Мн.; Навука i тэхніка, 1992.
2. Кашулин С. М., Дымовский А. С. Установка электроконтактного нагрева // Вопросы обработки металлов и сплавов. Мн.: Наука и техника, 1975.
3. Прозоров Л. В. Прессование стали и тугоплавких сплавов. М.: Машиностроение, 1969.
4. Вайнблат Ю. М., Горохов В. Н. и др. Основы получения штамповок из алюминиевых сплавов с полигонизованной структурой // Металловедение и технология легких сплавов. М.: Наука, 1976.
5. Отчет о НИР “Исследование прочностных и пласти¬ческих характеристик сплавов Д16 и АМгб”. ВИНИТИ. №02840087066.
6. Анисович А. Г., Тофпенец Р. Л. Специфика структурообразования в алюминиевых сплавах при термоциклировании // Изв. РАН. Металлы. 2000. №2. С.73—78.
Review
For citations:
Topfenets R., Anisovich A.G., Vasiljeva L.A. Study of the possibility of plasticity increase of cast alloy D16. Litiyo i Metallurgiya (FOUNDRY PRODUCTION AND METALLURGY). 2002;(3):30-34. (In Russ.)
Views:
1805
Email this article 