Structure and properties of iron shot heat-treated during induction heating, produced at MAZ
Abstract
The investigation results of structure and properties of iron shot of MAZ production in as-cast condition and after tempering during induction heating to 280—450 °C are presented. It is shown that during induction heating tempering processes run completely during 5—7minutes' heating. Due to tempering, in purification operations durability raises by 3—5 times.
About the Authors
P. S. Gurchenko
Minsk Automobile Plant
Belarus
Belarus
M. I. Demin
Minsk Automobile Plant
Belarus
Belarus
N. A. Simonov
Minsk Automobile Plant
Belarus
Belarus
D. A. Volkov
Institute BelNIIlit
Belarus
Belarus
V. L. Rassudov
Institute BelNIIlit
Belarus
Belarus
References
1. Рассудов В. Л., Шмидт В. И., Швецов Л. В. Изготовление литой дроби на малогабаритных машинах мод. 4678 // Литейное производство. 1995. № 3. С. 30—32.
2. Ефимов Ф. Т., Фролов Н. Г. Металлические дробь и песок. Производство и применение. М.: Машгиз, 1963.
3. Волков Д. А., Мельников А. П., Рассудов В. Л. и др. //Литейное производство. 2000. № 12, С. 21—22.
4. Дробь чугунная и стальная техническая. ГОСТ 11964—81.
Review
For citations:
Gurchenko P.S., Demin M.I., Simonov N.A., Volkov D.A., Rassudov V.L. Structure and properties of iron shot heat-treated during induction heating, produced at MAZ. Litiyo i Metallurgiya (FOUNDRY PRODUCTION AND METALLURGY). 2001;(4):58-61. (In Russ.)
Views:
257
Email this article 