THERMO-MECHANICALLY PROCESSED ROLLED WIRE FOR HIGH
Abstract
It is shown that at twisting of wire of diameter 1,83 mm, produced by direct wire drawing of thermomechanically processed rolled wire of diameter 5,5 mm of steel 90, metal stratification is completely eliminated at decrease of carbon, manganese and an additional alloying of chrome.
About the Authors
V. A. Lutsenko
Iron and Steel Institute of NAS Ukraine
Ukraine
Ukraine
V. G. Chernichenko
Iron and Steel Institute of NAS Ukraine
Ukraine
Ukraine
V. G. Lutsenko
Iron and Steel Institute of NAS Ukraine
Ukraine
Ukraine
I. N. Radjkova
BMZ – management company of holding «BMK»
Belarus
Belarus
References
1. Toshimi T. Microstructure control and strengthening of steel cord // Ferrum. 2006. Vol. 11. N 12. P. 791–797.
2. Гудремон Э. Специальные стали / Пер. с нем. Изд. 2-е сокр. и перераб. Т. ІІ. М.: Металлургия, 1966. С. 519.
3. Влияние термомеханической обработки и легирования на формирование свойств в высокоуглеродистой катанкепроволоке / В. А. Луценко, В. А. Маточкин, Ю. Л. Худолей и др. // Сталь. 2010. № 9. С.76–78.
4. Уикс К. Е., Блок Ф. Е. Термодинамические свойства 65 элементов, их оксидов, карбидов и нитридов. М.: Металлургия, 1965.
Review
For citations:
Lutsenko V.A., Chernichenko V.G., Lutsenko V.G., Radjkova I.N. THERMO-MECHANICALLY PROCESSED ROLLED WIRE FOR HIGH. Litiyo i Metallurgiya (FOUNDRY PRODUCTION AND METALLURGY). 2012;(4):57-59. (In Russ.)
Views:
424
Email this article 