Selection of the optimal version of the rolling rings of stand no. 7 of mill 150 of OJSC “BSW Management Company of Holding “BMC” from various types of high-speed steel, providing the best indicator of operational durability

Rolling rings as an important element of the rolling mill belong to the category of replaceable equipment, the quality of performance of which affects a number of operational characteristics, as well as the quality of rolled products. The material from which the rolling ring of the stand No. 7 is made must have the appropriate properties capable of perceiving high thermal loads for a long period of time without destruction, chipping and significant development of calibers. In this regard, there is a need to select the optimal option for the manufacture of rolling rings that can withstand such loads for a sufficiently long period of time. The study of the causes of destruction of the rolling ring 450×242×100 mm of high-speed steel, used at OJSC «BSW – Management Company of the Holding «BMC» in the cage number 7 mill 150 rolling shop. The results of metallographic studies of the microstructure and chemical composition of fragments of the destroyed rolling ring are presented. A detailed study and comparative analysis of the chemical composition and microstructure of samples of similar rings made of high-speed steel from two different suppliers, which showed high results in durability during operation, was carried out.

1. Shestopalova L. P., Lihacheva T. E. Metody issledovanija materialov i detalej mashin pri provedenii avtotehnicheskojj ekspertizy [Methods of researching materials and machine parts during automotive technical examination]. Moscow, MADI Publ., 2017, 180 p.

2. www.metaljournal.com.ua/high-speed-steel-2

3. Revis I. A., Lebedev T. A. Struktura i svojstva litogo rezhushhego instrumenta [Structure and properties of cast cutting tools.]. Leningrad, Mashinostroenie Publ., 1972.