Plasma coatings made of mechanically synthesized composite powders based on the «iron-aluminum» system

https://doi.org/10.21122/1683-6065-2020-3-84-92

Abstract

The regularities of the formation of plasma coatings obtained from powders based on the Fe-Al system synthesized by the reaction mechanical alloying method are established. The influence of the processing modes of the compositions in the mechanoreactor on the properties of coatings is revealed. An effective method for controlling the porosity of coatings from developed powders based on a change in the power consumed by the installation is proposed.

Plasma coatings have a nonequilibrium phase composition, which, in contrast to the equilibrium one, contains a wide range of metal oxides of the base and alloying elements formed during the spraying. The coating retains submicra – microcrystalline type of structure of powders with a highly developed grain and subgrain boundary. The basis of the coating is intermetallic FeAl. The role of hardening phases is played by ultrafine compounds of intermetallics and oxides.

Powder annealing has a significant effect on the structure and properties of coatings and, first of all, on layers from compositions with complex alloying with oxides. Heat treatment increases the density and hardness of coatings and reduces porosity. The study of coating samples after high temperature indicates high heat resistance and the preservation of the microcrystalline type of structure of their bases.

About the Authors

F. G. Lovshenko
Belarusian-Russian University
Belarus
Mogilev, Belarus, 43, Mira Ave.


A. S. Fedosenko
Belarusian-Russian University
Belarus
Mogilev, Belarus, 43, Mira Ave.


References

1. Lovshenko F.G., Fedosenko A. S. Fazovyj sostav, struktura i svojstva zharoprochnyh poroshkov na osnove sistemy «zhelezoaljuminij», poluchennyh po tehnologii reakcionnogo mehanicheskogo legirovanija [Phase composition, structure and properties of heat‑resistant powders based on the iron‑aluminum system obtained by the technology of reactive mechanical alloying]. Lit’e i metallurgija = Foundry production and metallurgy, 2019, no. 3, pp. 133–141.

2. Amils X. et al. Hardening and softening of FeAl during milling and annealing. Intermetallics, 2000, no. 8, pp. 805–813.

3. Enzo S. et al. Structural transformation of Al‑Fe alloys analysed by neutron diffraction and Mössbauer spectroscopy. Journal of Materials Science, 2004, no. 20, vol. 39, pp. 6333–6339.

4. Gialanella S. et al. Microstructural and kinetic aspects of the transformations induced in a feal alloy by ball‑milling and thermal treatments. Actamateriala, 1998, no. 9, vol. 46, pp. 3305–3316.

5. Amils X. et al. Structural, mechanical and magnetic properties of nanostructured FeAl alloys during disordering and thermal recovery. NanoStructured Materials, 1999, no. 6, vol. 11, pp. 689–695.

6. Hanc A. et al. Mössbauer and structure studies on metallic powders from Fe‑Al‑X (X = Ni, Cu, Cr). Archives of Materials Science and Engineering, 2008, vol. 31, Issue 1, pp. 21–24.

7. Rosas G. et al. Electron microscopy and x‑ray diffraction characterization of FeAl – BN nanocomposites produced by mechanical alloying. ActaMicroscopica, 2010, no. 3, vol. 19, pp. 285–290.

8. Lovshenko F. G., Lovshenko G. F. Zakonomernosti formirovanija fazovogo sostava, struktury i svojstv mehanicheski legirovannyh materialov [Patterns of formation of phase composition, structure and properties of mechanically alloyed materials]. Mogilev, Belorussko‑Rossijskij universitet Publ., 2016, 420 p.

9. Lovshenko G.F., Lovshenko F. G. Teoreticheskie i tehnologicheskie aspekty sozdanija nanostrukturnyh mehanicheski legirovannyh materialov na osnove metallov [Theoretical and technological aspects of creating nanostructured mechanically alloyed materials based on metals]. Mogilev, Belorussko‑Rossijskij universitet Publ., 2005, 276 p.

10. Lovshenko F. G., Fedosenko A. S. Mehanicheski legirovannye zharoprochnye poroshki dlja proizvodstva izdelij additivnymi tehnologijami [Mechanically alloyed heat‑resistant powders for the manufacture of products by additive technologies]. Mogilev, Belorussko‑Rossijskij universitet, 2019, 405 p.

11. Lovshenko F. G., Lovshenko G. F., Fedosenko A. S. Zakonomernosti strukturno‑fazovyh prevrashhenij v mehanicheski legirovannyh poroshkah i plazmennyh pokrytijah iz nih [Patterns of structural‑phase transformations in mechanically alloyed powders and plasma coatings from them]. Vestnik Belorussko-Rossijskogo universiteta = Bulletin of the Belarusian-Russian University, 2017, no. 1 (54), pp. 31–46.

12. Lovshenko F. G., Lovshenko G. F., Fedosenko A. S. Vlijanie mehanicheskogo legirovanija na fazovyj sostav i teplosoderzhanie termoreagirujushhih poroshkovyh kompozicij na osnove zheleza i nikelja dlja gazotermicheskih pokrytij [The effect of mechanical alloying on the phase composition and heat content of thermosetting powder compositions based on iron and nickel for gas‑thermal coatings]. Lit’e i metallurgija = Foundry production and metallurgy, 2014, no. 4 (77), pp. 99–108.

13. Lovshenko F.G., Fedosenko A. S. Svojstva plazmennyh pokrytij iz mehanicheski legirovannyh poroshkov na osnove metallov [Properties of plasma coatings of mechanically alloyed powders based on metals]. Metallurgija mashinostroenija = Metallurgy engineering., 2019, no. 4, pp. 20–24.

14. Lovshenko F. G., Lovshenko G. F., Fedosenko A. S. Zakonomernosti strukturno‑fazovyh prevrashhenij v mehanicheski legirovannyh poroshkah i plazmennyh pokrytijah iz nih [Patterns of structural‑phase transformations in mechanically doped powders and plasma coatings from them]. Vestnik Belorussko-Rossijskogo universiteta = Bulletin of the Belarusian-Russian University, 2017, no. 1 (54), pp. 31–46.


Review

For citations:


Lovshenko F.G., Fedosenko A.S. Plasma coatings made of mechanically synthesized composite powders based on the «iron-aluminum» system. Litiyo i Metallurgiya (FOUNDRY PRODUCTION AND METALLURGY). 2020;(3):84-92. (In Russ.) https://doi.org/10.21122/1683-6065-2020-3-84-92

Views: 1951


Creative Commons License
This work is licensed under a Creative Commons Attribution 4.0 License.


ISSN 1683-6065 (Print)
ISSN 2414-0406 (Online)