Study of changes in the structure of zirconium alloy E125 after deformation by radial shear rolling

The rheological properties of the alloy E125 (Zr‑2.5 %Nb) were studied in the range of deformation rates 0.5–15 s‑1 and the temperature range 20–770 °C. A database for computer FEM modeling was created in the specified temperature and speed ranges. In the DEFORM‑3D software package, numerical simulation of a complex radial shear rolling process was carried out using the obtained database. The conditions conducive to the grinding of the alloy structure into an ultrafine‑grained state were determined. Based on the simulation results, a full‑scale experiment of rolling a bar made of alloy E125 on a radial shear rolling mill RSP‑14/40 in 7 passes from a diameter of 37 mm to 20 mm with a total compression in diameter of ε = 85 % was carried out. At the same time, according to the modeling, the total accumulated deformation in the most developed peripheral zone was 27,5 mm/mm. Due to the complex vortex flow of the metal, the distribution of accumulated deformation over the cross section was uneven with a gradient to the axial zone. This should also affect the change in the structure. The changes and the gradient of the structure were studied by the method of EBSD mapping of the sample section with a resolution of 2 mm. The microhardness gradient of the cross section was also investigated by the HV method. The axial and central zones of the sample were studied on the. The structure has a pronounced gradient from the formed equiaxed ultrafine‑grained (UMZ) structure on several outer millimeters of the peripheral section to an elongated rolling texture in the center of the rod. The work shows the possibility of processing with the formation of a gradient structure with enhanced properties for the E125 alloy, and also presents a database for FEM calculations.

1. Bronnikov V.A. Ezhegodnyj obzor mirovogo sostojanija jadernoj promyshlennosti [Annual review of the world state of the nuclear industry]. Atomnaja tehnika za rubezhom = Nuclear technology abroad, 2003, no. 9, pp. 17–25.

2. Millard J. W. F., Dimitrov L., Bajwa D. ACR‑1000 Fuel Channel Developments. Presented at: International Conference on Advances in Nuclear Materials: Processing, Performance and Phenomena ANM‑2006. December 12–16, 2006.

3. Abramov M.A., Avdeev V. I., Adamov E. O. Kanal’nyj jadernyj jenergeticheskij reaktor RBMK [Channel nuclear power reactor RBMK]. Moscow, GUP NIKIJeT Publ., 2006, 632 p.

4. Coleman C. E., Cheadle B.A., Cann C. D., Theaker J. R. Development of Pressure Tubes with Service Life Greater Than 30 Years. Zirconium in the Nuclear Industry: Eleventh International Symposium, ASTM STP 1295, 1996, pp. 884–898.

5. Nekrasova G. F. Opyt jekspluatacii kanal’nyh trub v reaktorah CANDU. Cirkonij v atomnoj promyshlennosti [Experience in the operation of channel pipes in CANDU reactors. Zirconium in the nuclear industry]. Moscow, CNII Atominform Publ., 1985, no. 14, 36 p.

6. Zazhmovskij A. S., Nikulina A. V. i dr. Cirkonievye splavy v jadernoj jenergetike [Zirconium alloys in nuclear power]. Moscow, Jenergoatomizdat Publ., 1994, 256 p.

7. Mozzani N., Auzoux Q., Le Boulch D., Andrieu E., Blanc C., Scott C. P., Barnel N. Mechanical behavior of recrystallized Zircaloy‑4 under monotonic loading at room temperature: Tests and simplified anisotropic modeling. Journal of Nuclear Materials, 2014, no. 447, pp. 94–106.

8. Kudrjashov S. I., Kolobov Ju. R., Ivanov M. B., Golosov E. V. Perspektivy razrabotki korrozionno‑ustojchivyh nanostrukturnyh i submikrokristallicheskih materialov na baze titanovyh i cirkonievyh splavov, nerzhavejushhej stali, s modificirovannoj poverhnost’ju [Prospects for the development of corrosion‑resistant nanostructured and submicrocrystalline materials based on titanium and zirconium alloys, stainless steel, with a modified surface]. Innovatika i jekspertiza = Innovation and expertise, 2013, no. 1(10), pp. 82–91.

9. Nikulin S.A., Rogachev S. O., Rozhnov A. B., Kopylov V. I., Dobatkin S. V. Korrozionnaja povrezhdaemost’ pri KRN ispytanijah splava Zr‑2,5Nb, podvergnutogo ravnokanal’nomu uglovomu pressovaniju [Corrosion damage during SCC tests of Zr‑2.5Nb alloy subjected to equal‑channel angular pressing]. Fizika i himija obrabotki materialov = Physics and chemistry of material processing, 2012, no. 1, pp. 74–79.

10. Valiev R. Z., Islamgaliev R. K., Alexandrov I. V. Bulk nanostructured materials from severe plastic deformation. Prog. Mater. Sci, 2000, no. 45, pp. 103–189.

11. Galkin S. P. Radial shear rolling as an optimal technology for lean production. Steel in Translation, 2014, no. 44, pp. 61–64.

12. Аrbuz A., Kawalek A., Ozhmegov K., Sultanbekov S., Shamenova R. Using of radial‑shear rolling to improve the structure and radiation resistance of zirconium‑based alloys. Materials, 2020, vol. 13(19), no. 4306, pp. 1–15.

13. Kawałek A., Dyja H., Gałkin A. M., Ozhmegov K. V., Sawicki S. Physical modelling of the plastic working processes of zirconium alloy bars and tubes in thermomechanical conditions. Archives of Metallurgy and Materials, 2014, no. 59(3), pp. 935–940.

14. Kawałek A., Gałkin A., Dyja H., Knapiński M. J., Koczurkiewicz B. Plastometric modelling of the E635M zirconium alloy multistage forging process. Solid State Phenomena, 2015, no. 220–221, pp. 808–812.

15. Banerjee S., Mukhopadhyay P. Phase Transformations: Examples from Titanium and Zirconium Alloys. Elsevier Ltd., 2007, pp. 359–374.