DESTRUCTION OF GRAPHITIZED STEELS AT CYCLIC LOAD
Abstract
It is determined that graphitized steels are perspective construction material, the breakage resistance and mechanical characteristics of which are determined to a considerable degree by form of graphitic impurities.
About the Authors
I. P. Volchok
Zaporizhzhya National Technical University
Ukraine
Ukraine
I. V. Akimov
Zaporizhzhya National Technical University
Ukraine
Ukraine
A. A. Mitjaev
Zaporizhzhya National Technical University
Ukraine
Ukraine
I. M. Andrejko
Karpenko Physico-Mechanical Institute of the NAS of Ukraine
Ukraine
Ukraine
N. A. Svidunovich
Belarusian State Technological University
Belarus
Belarus
S. E. Belskij
Belarusian State Technological University
Belarus
Belarus
D. V. Kuis
Belarusian State Technological University
Belarus
Belarus
A. P. Melnikov
BELNIILIT
Belarus
Belarus
M. A. Sadoha
BELNIILIT
Belarus
Belarus
References
1. Литовка В. И., Бех Н. И., Шинский О. И. Усталостная прочность и разрушение чугуна // Литейное производство. 1994. №6. С. 3–8.
2. Волчок И. П., Колотилкин О. Б., Шейко С. П. Конструкционные материалы для стеклоформующего инструмента. Запорожье: Издательский центр «Павел», 1997.
3. Механика разрушения и прочность материалов: Справ. пособ. в 4-х т. Киев: Наукова думка, 1990.
4. Осташ О. П., Костик Є. М., Андрейко І. М., Дронюк М. М. Вплив мікроструктури на низькотемпературну циклічну тріщинотривкість високоміцних чавунів // Фізико-хімічна механіка руйнування. 1997. № 1. С. 57–69.
Review
For citations:
Volchok I.P., Akimov I.V., Mitjaev A.A., Andrejko I.M., Svidunovich N.A., Belskij S.E., Kuis D.V., Melnikov A.P., Sadoha M.A. DESTRUCTION OF GRAPHITIZED STEELS AT CYCLIC LOAD. Litiyo i Metallurgiya (FOUNDRY PRODUCTION AND METALLURGY). 2010;(4):58-61. (In Russ.)
Views:
2006
Email this article 