IMPROVEMENT OF EFFICIENCY OF GREY CAST IRON MODIFICATION DUE TO INTRODUCTION OF CARBON MODIFIER INTO COMPOSITION
https://doi.org/10.21122/1683-6065-2010-3-47-50
Abstract
It is shown that introduction carbon into modifier composition and increase of its dispersion degree due to spatter on high-melting particles or due to mechanical alloying increases modifier efficiency for grey cast iron.
About the Authors
G. F. Lovshenko
Belarusian National Technical University
Belarus
Belarus
O. S. Komarov
Belarusian National Technical University
Belarus
Belarus
N. I. Urbanovich
Belarusian National Technical University
Belarus
Belarus
V. I. Volosatikov
Belarusian National Technical University
Belarus
Belarus
V. S. Niss
Belarusian National Technical University
Belarus
Belarus
A. I. Letsko
Powder Metallurgy Institute of the NAS of Belarus
Belarus
Belarus
Review
For citations:
Lovshenko G.F., Komarov O.S., Urbanovich N.I., Volosatikov V.I., Niss V.S., Letsko A.I. IMPROVEMENT OF EFFICIENCY OF GREY CAST IRON MODIFICATION DUE TO INTRODUCTION OF CARBON MODIFIER INTO COMPOSITION. Litiyo i Metallurgiya (FOUNDRY PRODUCTION AND METALLURGY). 2010;(3):47-50. (In Russ.) https://doi.org/10.21122/1683-6065-2010-3-47-50
Views:
1568
Email this article 