THE EXPERIENCE OF THE INDUSTRIAL DEVELOPMENT OF STEEL 20A PRODUCTION TECHNOLOGY FOR THE HOT-ENHANCED CORROSION RESISTANCE AND COLD RESISTANCE SEAMLESS PIPES
Abstract
Experimental melting of the grade 20A steel during which desulfurization degree from 88 to 94% is reached, is carried out at ESPTs-2 of JSC «BMZ». The content of sulfur in teeming assay [S]82 = 0,0015% and correlation [Ca]/[S] =1,46 are reached at melting with application of «pure burden» and double induction of refining ladle slag.
About the Authors
A. S. Zazyan
BMZ – management company of holding «BMK»
Belarus
Belarus
S. V. Terletskii
BMZ – management company of holding «BMK»
Belarus
Belarus
References
1. Внутренняя коррозия трубопроводов – причины, механизм и способы защиты. Материалы сайта OILLOOT. RU
2. Teresa E. Perez, CINI Siderca; Hector Quintanilla, Tubos de Acero de Mexico SA; Eduardo Rey, SIDERCA. Effect of Ca/S Ratio on HIC Resistance of Seamless Line Pipes. // CORROSION 98, March 22–27, 1998, San Diego Ca
3. Производство стали. Т. 3. Внепечная металлургия стали / Д. А. Дюдкин, В. В. Кисиленко. М.: Теплотехник, 2008.
4. Карья Я., Невапи Х., Хицуен У. и др. Характеристика износа огнеупоров при разливке сталей, раскисленных кальцием // Металлургический завод и технология. 1994. С. 24–28.
5. Информационный отчет ОАО «Самарский ИТЦ» «Оценка качества металла бесшовных нефтегазопроводных труб Ø114х7мм из стали 20А, производства ОАО «БМЗ», изготовленных по ТУ 1317-006.1-593377520-2003», Самара, 2013.
Review
For citations:
Zazyan A.S., Terletskii S.V. THE EXPERIENCE OF THE INDUSTRIAL DEVELOPMENT OF STEEL 20A PRODUCTION TECHNOLOGY FOR THE HOT-ENHANCED CORROSION RESISTANCE AND COLD RESISTANCE SEAMLESS PIPES. Litiyo i Metallurgiya (FOUNDRY PRODUCTION AND METALLURGY). 2013;(3):58-62. (In Russ.)
Views:
448
Email this article 